EVA CARRIEREconomic
WMB-EVA7025E70% rutile titanium dioxide in a EVA-18J3 carrier for EVA foam shoe materials and related EVA compounds, with a neutral undertone.
70%TiO₂content
NeutralUndertone
WMB / EVAMaterial illustration
WHITE MASTERBATCH
WMB-EVA7025A
AnataseEVAHigh whiteness
WMB-EVA7025A is a anatase white masterbatch containing 70% anatase titanium dioxide, pre-dispersed in a EVA-18J3 carrier. It is designed for EVA foam shoe materials and related EVA compounds, where carrier compatibility, pigment loading and visual undertone need to be considered together. Its high whiteness undertone provides a starting point for balancing opacity and final appearance. Confirm let-down ratio, dispersion, processing stability and finished-part performance through trials in your own formulation.
KNOW YOUR MATERIAL
Technical specifications.
| Parameter | Value |
|---|---|
| Appearance | White granules |
| Carrier resin | EVA-18J3 |
| Carrier content | 25% |
| TiO₂ content | 70% |
| Crystal type | Anatase |
| Undertone | High whiteness |
| Density | 1.6 g/cm³ |
| Bulk density | 1.02 g/cm³ |
| Moisture, maximum | 0.17% |
| Weight of 100 pellets | 2–4 g |
| PE wax | 3.5% |
| Zinc stearate | 1.5% |
Processing guidance
| Parameter | Value |
|---|---|
| Foaming pressure | 5–20 MPa |
| Melt temperature | Confirm before use |
| Mold temperature | 50–60 °C |
| Drying | 3 h at 60–80 °C |
Physical values are typical averages. Confirm suitability through trials in your resin and processing conditions.
Melt flow rate is not published here because the supplied unit and test conditions need confirmation.
The melt-temperature range in the supplied sheet is incomplete and must be confirmed before processing.